Journal of Shenzhen University Science and Engineering (深圳大学学报理工版) 2019/36:1 PP.94-100

Investigation on current effectiveness in the process of current accelerated corrosion of reinforcing steel


Abstract:
Impressed-current accelerated corrosion has been widely used in the study of steel corrosion. To investigate the actual consumption of impressed current during the accelerated corrosion process, micro-level X-ray computed tomography (XCT) technique is employed to trace the accelerated corrosion process of steel in a mortar sample to quantitatively analyze the mass loss of steel at different stages, with which current effective coefficient of each stage can be further calculated. The experiment results show that XCT technique can achieve non-destructive tracking of the corrosion process, visual characterization of corrosion morphology, and quantitative calculation of corrosion parameters. The calculation of current effective coefficient indicates that due to the influence of depassivation of steel, electrolysis of water and natural corrosion, the current effective coefficient varies in different corrosion stages. Before the cracking of concrete cover, depassivation and electrolysis lower the coefficient. After cracking, the coefficient is magnified by natural corrosion.

Key words:building materials,reinforced concrete,impressed-current accelerated corrosion,current effective coefficient,X-ray computed tomography

ReleaseDate:2019-01-28 09:56:36



[1] 刘昱清, 董鹏, 滕晓娟,等. 基于X-ray μCT技术的钢筋锈胀特征分析[J]. 深圳大学学报理工版,2017,34(6):618-624. LIU Yuqing, DONG Peng, TENG Xiaojuan, et al. Characterization of corrosion expansion feature of steel bar by means of X-ray μCT[J]. Journal of Shenzhen University Science and Engineering,2017,34(6):618-624.(in Chinese)

[2] 赵娟, 李蓓. 温湿-氯离子耦合渗透跨海大桥寿命预测模型[J]. 深圳大学学报理工版,2015,32(6):632-637. ZHAO Juan, LI Bei. Life prediction model of cross-sea bridge considering chloride ion penetration coupled with temperature and moisture transfer[J]. Journal of Shenzhen University Science and Engineering,2015,32(6):632-637.(in Chinese)

[3] DEMIS S, PILAKOUTAS K, APOSTOLOPOULOS C A. Effect of corrosion on bond strength of steel and non-metallic reinforcement[J]. Materials and Corrosion,2010,61(4):328-31.

[4] XU Aimin, SHAYAN A. Relationship between reinforcing bar corrosion and concrete cracking[J]. ACI Materials Journal,2016,113(1):3-12.

[5] SANZ B, PLANAS J, SANCHO J M. Study of the loss of bond in reinforced concrete specimens with accelerated corrosion by means of push-out tests[J]. Construction and Building Materials,2018,160:598-609.

[6] JAFFERJI H, SAKULICH A R, SCHIFFMAN J D. Preliminary study on mitigating steel reinforcement corrosion with bioactive agent[J].Cement and Concrete Composites,2016,69:9-17.

[7] APOSTOLOPOULOS C A, DEMIS S, PAPADAKIS V G. Chloride-induced corrosion of steel reinforcement:mechanical performance and pit depth analysis[J]. Construction and Building Materials,2013,38:139-146.

[8] 薛斌, 孙启荣, 王辰宇, 等. 腐蚀钢筋混凝土结构研究现状及展望[J]. 能源与环保,2017,39(4):174-179. XUE Bin, SUN Qirong, WANG Chenyu, et al. Recent research and prospect on corroded reinforced concrete structure[J]. China Energy and Environmental Protection,2017,39(4):174-179.(in Chinese)

[9] 施锦杰, 孙伟. 混凝土中钢筋锈蚀研究现状与热点问题分析[J]. 硅酸盐学报,2010,38(9):1753-1764. SHI Jinjie, SUN Wei. Recent research on steel corrosion in concrete[J]. Journal of the Chinese Ceramic Society,2010,38(9):1753-1764.(in Chinese)

[10] DEHAOUX A, BOUCHELAGHEM F, BERTHAUD Y. Micromechanical and microstructural investigation of steel corrosion layers of variable age developed under impressed current method, atmospheric or saline conditions[J]. Corrosion Science,2015,97:49-61.

[11] NOSSONI G, HARICHANDRAN R. Current efficiency in accelerated corrosion testing of concrete[J]. Corrosion,2012,68(9):801-809.

[12] SUN Hongfang, ZHAO Diandain, GU Yang, et al. Three-dimensional characterization of steel corrosion embedded in cement paste[J]. Construction and Building Materials,2017,143:24-32.

[13] LAW D W, MOLYNEAUX T C K. Impact of corrosion on bond in uncracked concrete with confined and unconfined rebar[J].Construction and Building Materials,2017,155:550-559.

[14] 干伟忠, 金伟良, 高明赞. 混凝土中钢筋加速锈蚀试验适用性研究[J]. 建筑结构学报,2011,32(2):41-47. GAN Weizhong, JIN Weiliang, GAO Mingzan. Applicability study on accelerated corrosion methods of steel bars in concrete structure[J]. Journal of Building Structures,2011,32(2):41-47.(in Chinese)

[15] BECK M, GOEBBELS J, BURKERT A, et al. Monitoring of corrosion processes in chloride contaminated mortar by electrochemical measurements and X-ray tomography[J]. Materials and Corrosion,2010,61(6):475-479.

[16] LANDIS E N, KEANE D T. X-ray microtomography[J]. Materials Characterization,2010,61(12):1305-1316.

[17] HSIEH C H. Procedure and analysis of mineral samples using high resolution X-ray micro tomography[D]. Utah,USA:University of Utah,2012.

[18] DONG Biqin, FANG Guohao, LIU Yuqing, et al. Monitoring reinforcement corrosion and corrosion-induced cracking by X-ray microcomputed tomography method[J]. Cement and Concrete Research,2017,100:311-321.

[19] 杨晓明, 吴天宇, 陈永林. 人工加速锈蚀钢筋混凝土构件中钢筋锈蚀率与锈蚀电流的关系研究[J]. 硅酸盐通报,2016,35(10):3410-3416. YANG Xiaoming, WU Tianyu, CHEN Yonglin. Relationship between the current and corrosion ratio in corroded reinforced concrete component obtained by artificial accelerated corrosion method[J]. Bulletin of the Chinese Ceramic Society,2016,35(10):3410-3416.(in Chinese)

[20] 金伟良, 岳增国, 许晨, 等. 混凝土中钢筋脱钝氯离子阈值的快速测定[J]. 中国腐蚀与防护学报,2012,32(3):223-227. JIN Weiliang, YUE Zengguo, XU Chen, et al. Accelerated simultaneous determination of chloride depassivation threshold of rebar in concrete[J]. Journal of Chinese Society for Corrosion and Protection,2012,32(3):223-227.(in Chinese)

[21] DUFFO G, GAILLARD N, MARISCOTTI M, et al. Application of gamma-ray radiography and gravimetric measurements after accelerated corrosion tests of steel embedded in mortar[J]. Cement and Concrete Research, 2015,74:1-9.

[22] 袁迎曙, 章鑫森, 姬永生. 人工气候与恒电流通电法加速锈蚀钢筋混凝土梁的结构性能比较研究[J]. 土木工程学报,2006,39(3):42-46. YUAN Yingshu, ZHANG Xinsen, JI Yongsheng. A comparative study on structural behavior of deteriorated reinforced concrete beam under two different environments[J]. China Civil Engineering Journal,2006,39(3):42-46.(in Chinese)